iglidur® B - Material data

Materials table

Genera l features	Unit	iglidur® B	test method
Density	g/cm³	1,15
Colour		Gray
Max. humidity absorption at 23°C/50% R. H.	% weight	1,0	DIN 53495
Max. water absorption	% weight	6,3
Coefficient of surface friction, dynamic, against steel	μ	0,18–0,28
pv value, max. (dry)	MPa x m/s	0,15
Mechanical properties
Bending E-module	MPa	1.800	DIN 53457
Tensile strength at +20 °C	MPa	55	DIN 53452
compressive strength	MPa	20
Maximum recommended surface pressure (20° C)	MPa	40
Shore D-hardness		69	DIN 53505
Physical and thermal properties
Max. long term application temperature	°C	+100
Max. short term application temperature	°C	+130
Minimum application temperature	°C	-40
thermal / heat conductivity	W/m x K	0,24	ASTM C 177
Coefficient of thermal expansion (at 23° C)	K^–1 x 10^–5	12	DIN 53752
Electrical properties
Specific forward resistance	Ωcm	> 10¹⁰	DIN IEC 93
surface resistance	Ω	> 10⁹	DIN 53482

'Table 01: Material Data

The compressive strength of the iglidur® B bearings is on the one hand low, but on the other, is an important property of the bearing. They are mainly used where vibration dampening and acoustic separation are required.

Figure 02: Maximum recommended surface pressure dependent on the temperature (40 MPa to +20 °C)

X = Temperature [°C]
Y = Load [MPa]

Figure 03: Deformation under load and temperatures

X = Load [MPa]
Y = Deformation [m/s]

Mechanical properties

Maximum recommended surface pressure represents a mechanical material parameter. Tribological conclusions cannot be drawn from it. The pressure resistance of iglidur® B bearings declines with increasing temperatures. Fig. 02 clarifies this connection.

The deformation at 40 MPa at room temperature is 5.3% (Fig. 03).

Maximum surface speed

m/s	Rotating	Oscillating	Linear
Constant	0,7	0,5	2
Short-term	1	0,7	3

Permitted surface speeds

iglidur® B bearings can be continuously used up to 0.7 m/s. The frictional heat provides the speed limits.

Surface speed

p x v value and lubrication

Figure 22.3: Maximum recommended surface pressure dependent on the temperature

Temperatures

The operating temperature of the iglidur® B bearings is limited to 100° C. From 50° C onward, the very soft bearing should be mechanically fastened, so that the danger of bushings creeping out of the bores is avoided. The wear resistance too declines disproportionately from 70° C.

Temperatures, coefficient of thermal expansion

Figure 2.4: Coefficients of friction dependent on the surface speed, p = 0.75 MPa

Figure 05: Coefficients of friction dependent on the load, v = 0,01 m/s

X = Load [MPa]
Y = Coefficient of friction μ

Friction and wear

The coefficients of friction increase slightly with the speed and decrease with the load. Shaft surface finishes between 0.4 and 0.6 Ra are ideal. Providing the bearing load is not too high, the attained coefficients of wear are very good. An increase in load results in a disproportionate increase in abrasion.

Coefficients of friction for iglidur® B against steel
(Ra = 1 µm, 50 HRC)

iglidur® B	Dry	Grease	Oil	Water
Coefficients of friction µ	0,18 - 0,28	0,09	0,04	0,04

Coefficients of friction

Wear resistance

Figure 06: Wear, rotating application with different shaft materials, p = 1 MPa, v = 0.3 m/s

X = shaft materials
Y = wear [μm/km]

A = Aluminum, hard-anodized
B = machining steel
C = Cf53
D = Cf53, hard chrome-plated
E = St37
F = V2A
G = X90

Shaft materials

The influence of the shaft material is not very large in wear resistance.

Figures 06 and 07 clarify that very similar wear data are attained with different shaft materials. If high operational performances are expected, the bearing load should not be too high.

Shaft materials

Figure 07: Wear in pivoting and rotating applications with Cf53 dependent on the load

X = Load [MPa]
Y = Wear [μm/km]

A = Rotating
B = Pivoting

Figure 22.9: Wear with pivoting and rotating applications with Cf53 shaft material, dependent on the load

Medium	Resistance
Alcohol	+ to 0
Hydrocarbons	-
Fats, oils, without additives	-
Fuels	-
Diluted acids	0 to -
Strong acids	-
Diluted bases	-
Strong bases	-

+ resistant 0 conditionally resistant - non-resistant

Electrical properties

Specific forward resistance	> 10¹⁰ Ωcm
Surface resistance	> 10⁹ Ω

Chemical resistance

iglidur® B bearings are not very resistant to chemicals For chemical resistance, there are other iglidur® materials available with better properties.

Radioactive rays

iglidur® B bearings are radiation resistant up to a radioactive intensity of 3 x 10² Gy.

UV-resistant

iglidur® B bearings are not resistant to the influence of UV rays.

Vacuum

The use in vacuum is possible only conditionally. Only dry bearings made of iglidur® B should be tested in vacuum.

Electrical properties

Bearings made of iglidur® B are electrically insulating.

Maximum moisture absorption
by +23 °C/50 % r. F.	1,0 weight-%
Max. water absorption	6,3 weight-%

Table 06: Moisture absorption of iglidur® B

Effect of moisture absorption on plain bearings

Diagram 10: Effect of moisture absorption

X = Moisture absorption [weight %]
Y = Reduction of inside diameter [%]

humidity absorption / moisture absorption

The moisture absorption is relatively high and must be considered in the selection and design.

Important tolerances for iglidur® B bearings according to ISO 3547-1 after the press-fit.

Diameter d1 [mm]	Shaft h9 [mm]	iglidur® B D11 [mm]	Housing H7 [mm]
Up to 3	0 - 0,025	+0,020 +0,080	0 +0,010
> 3 to 6	0 - 0,030	+0,030 +0,105	0 +0,012
> 6 to 10	0 - 0,036	+0,040 +0,130	0 +0,015
> 10 to 18	0 - 0,043	+0,050 +0,160	0 +0,018
> 18 to 30	0 - 0,052	+0,065 +0,195	0 +0,021
> 30 to 50	0 - 0,062	+0,080 +0,240	0 +0,025
> 50 to 80	0 - 0,074	+0,100 +0,290	0 +0,030

Table 07: Important tolerances for iglidur® B bearings according to ISO 3547-1 after the press-fit.

Installation tolerances

iglidur® B bearings are standard bearings for shafts with h-tolerance (recommended minimum h9).

The bearings are designed for press-fit in a housing with h7 tolerance. After the installation in a housing with nominal diameter, the inner diameter of the bearing automatically adjusts to the D11 tolerance. In certain dimensions the tolerance in dependence on the wall thickness deviates from this (See delivery program )

Ülke/Bölge

Ülkenizi seçtiğinizde size yerel teklifler ve bilgiler gösterilecektir.

Dil ayarları

Tercih edilen dili seçin:

Teslimat noktanızı seçin

iglidur® B - Material data

Materials table

Mechanical properties

Maximum surface speed

Permitted surface speeds

Temperatures

Friction and wear

Coefficients of friction for iglidur® B against steel(Ra = 1 µm, 50 HRC)

Shaft materials

Electrical properties

Chemical resistance

Radioactive rays

UV-resistant

Vacuum

Electrical properties

humidity absorption / moisture absorption

Important tolerances for iglidur® B bearings according to ISO 3547-1 after the press-fit.

Installation tolerances

Ülke/Bölge

Dil ayarları

Page not found

Alışveriş sepeti

Alışveriş sepeti

Coefficients of friction for iglidur® B against steel
(Ra = 1 µm, 50 HRC)